Comparison of Porosity in Thermoplastic Filling Using MTA with Ca(OH)2 and MTA with Nano Chitosan by using Scanning Electron Microscope (SEM)

Authors

  • Dewa Made Wedagama Department of Conservative Dentistry, Faculty of Dentistry, Universitas Mahasaraswati Denpasar, Bali - Indonesia

DOI:

https://doi.org/10.46862/interdental.v21i2.12193

Keywords:

Porosity, Thermoplastic, MTA, Calcium Hydroxide, Nano Chitosan

Abstract

Introduction: Porosity often occurs after root canal treatment. Various sealers are used to close all the gaps between the root canal system and the outer surface of the tooth. The currently used root canal sealers include MTA, Ca(OH)₂, and nano chitosan (NC). The purpose of this study was to determine the difference in porosity levels of root canals treated with MTA sealer combined with Ca(OH)₂ versus MTA sealer combined with NC.

Method: This study used 16 human adult incisor samples (tooth #11), divided into two groups. The first group received MTA sealer with Ca(OH)₂, and the second group received MTA sealer with NC, both applied using the thermoplastic filling technique. After treatment, the samples were examined using scanning electron microscopy (SEM) to measure porosity.

Results: The porosity measurements (in micrometers, μm) for the first group (MTA with Ca(OH)₂) were: 12.24, 7.98, 9.81, 8.19, 10.85, 7.87, 8.43, and 8.96. The second group (MTA with NC) showed porosity values of: 7.73, 2.48, 6.80, 3.85, 1.32, 4.66, 3.98, and 4.22. The mean porosity in the first group was 9.29 μm, while in the second group it was 4.38 μm.

Conclusion: Statistical analysis showed a t-value of 5.31 with p < 0.001, indicating a significant difference between the two groups (p < 0.05). This suggests that MTA sealer combined with nano chitosan results in significantly lower porosity and better root canal filling density compared to MTA sealer combined with Ca(OH)₂.

Downloads

Download data is not yet available.

References

1. Ariani NGA, Hadriyanto W. Perawatan ulang saluran akar insisivus lateralis kiri maksila dengan medikamen kalsium hidroksida-chlorhexidine. Maj Kedokt Gigi Indones 2013; 20(1): 52-57.

2. Abdulwahab MA, Alqahtani MS, Alshammari AA, Jiffri SE, Alasim AM, Alsharidah FM, et al. Etiologies, risk factors, and outcomes of dental pulp necrosis. Int J Community Med Public Heal 2021; 9(1): 348. Doi: 10.18203/2394-6040.ijcmph20214793

3. Sampoerno G, Sukaton, Aulia Rahmawati S. Endodontic flare-up incidence in irreversible pulpitis in Universitas Airlangga Dental Hospital (RSKGMP Universitas Airlangga). Conserv Dent J 2022; 12(1): 26–31. Doi: 10.20473/cdj.v12i1.2022.26-31

4. Munirah M, Trilaksana AC, Nugroho JJ. Seal apikal dari sealer berbahan dasar resin epoksi dan berbahan dasar mineral trioxide aggregate (Apicalsealingofepoxyresin-basedandmineral trioxide aggregate-based root canal sealers). J Dentomaxillofacial Sci. 2014;13(3):170.

5. Murray PE. Review of guidance for the selection of regenerative endodontics, apexogenesis, apexification, pulpotomy, and other endodontic treatments for immature permanent teeth. Int Endod J 2023; 56(S2): 188–99. Doi: 10.1111/iej.13809

6. Kusuma ARP. Pengaruh lama aplikasi dan jenis bahan pencampur serbuk kalsium hidroksida terhadap kekerasan mikro dentin saluran akar. ODONTO Dent J 2016; 3(1): 48–54. Doi: 10.30659/odj.3.1.48-54

7. Ayu Rahaswanti LW. Evaluasi keberhasilan pengisian saluran akar dengan sediaan zinc oxide eugenol dan campuran calcium hydroxide dengan pasta iodoform. Intisari Sains Medis 2017; 8(1): 1–7. Doi: 10.1556/ism.v8i1.1

8. Bayram E, Bayram HM, Aslan T, Ustün Y. Does MTA and calcium hydroxide additives effect on the bond Strength of AH plus sealer. Res Rev J Dent Sci 2018; 6(1): 25–31.

9. Dzung NA, Khanh VTP, Dzung TT. Research on impact of chitosan oligomers on biophysical characteristics, growth, development and drought resistance of coffee. Carbohydr Polym 2011; 84(2): 751–5. Doi: 10.1016/j.carbpol.2010.07.066

10. Kebke S, Fransson H, Brundin M, Mota de Almeida FJ. Tooth survival following root canal treatment by general dental practitioners in a Swedish county – a 10-year follow-up study of a historical cohort. Int Endod J 2021 54(1): 5–14. Doi: 10.1111/iej.13392

11. Nagpal K, Singh SK, Mishra DN. Chitosan nanoparticles: A promising system in novel drug delivery. Chem Pharm Bull. 2010;58(11):1423–30. Doi: 10.1248/cpb.58.1423

12. Inajati I, Untara RTE. Apeksifikasi dengan mineral trioxide aggregate dan perawatan intracoronal bleaching pada gigi insisivus sentralis kiri maksila non vital diskolorasi. Maj Kedokt Gigi Indones 2016; 2(2): 101-8. Doi: 10.22146/majkedgiind.11251

13. El Hadrami A, Adam LR, El Hadrami I, Daayf F. Chitosan in plant protection. Mar Drugs 2010; 8(4): 968–87. Doi: 10.3390/md8040968

14. Büker M, Sümbüllü M, Ali A, Ünal O, Arslan H. The effects of calcium silicate- and calcium hydroxide–based root canal sealers on postoperative pain: A randomized clinical trial. J Endod 2023; 49(12): 1588–94. Doi: 10.1016/j.joen.2023.08.023

15. Drumond JPSC, Maeda W, Nascimento WM, Campos D de L, Prado MC, de-Jesus-Soares A, et al. Comparison of postobturation pain experience after apical extrusion of calcium silicate– and resin–based root canal sealers. J Endod 2021; 47(8): 1278–84. Doi: 10.1016/j.joen.2021.05.008

16. Kumar V, Abbas AK, Aster JC. Robbins and Cotran: Pathologic Basis of Disease. 9th Edition. Philadelphia: Elsevier; 2015. p. 1592

Downloads

Published

2025-08-05

How to Cite

1.
Wedagama DM. Comparison of Porosity in Thermoplastic Filling Using MTA with Ca(OH)2 and MTA with Nano Chitosan by using Scanning Electron Microscope (SEM) . interdental [Internet]. 2025 Aug. 5 [cited 2025 Aug. 8];21(2):265-8. Available from: https://e-journal.unmas.ac.id/index.php/interdental/article/view/12193

Most read articles by the same author(s)